Effects of sodium tungstate on characteristics of microarc oxidation coatings formed on magnesium alloy in silicate-KOH electrolyte

Oxide coatings on AM60B magnesium alloy were prepared using the microarc oxidation（MAO） technique in silicate-KOH electrolyte with addition of 0-6.0 g/L Na2WO4. The MAO processes in base electrolyte with different concentrations of Na2WO4 were studied. The microstructure, compositions and mechanical tribological characteristics of the oxide coatings were also investigated by SEM, XRD, XPS, microhardness analysis and ball-on-disc friction testing, respectively. It is found that the addition of Na2WO4 into the base electrolyte has direct effect on the characteristics of voltage-time curves and breakdown voltage in MAO process. The number of micropores at top of the coating surface is increased by the addition of Na2WO4. The fraction of forsterite Mg2SiO4 in the oxide coating increases with increasing concentration of Na2WO4 in base electrolytes. Furthermore, the microhardness and wear resistance of oxide coatings are enhanced as well.     

(Ⅰ+Ⅱ)复合型氢致开裂的研究

本文研究了30CrMnSiA高强钢在纯Ⅰ型、纯Ⅱ型和(Ⅰ+Ⅱ)复合型加载条件下的氢致开裂。实验表明,在1NH_2SO_4溶液中预充氢的试件在上述加载条件下均表现出氢致脆性。纯Ⅱ型氢致开裂门槛值K_(ⅡH)/K_(ⅡX)=0.27,与纯Ⅰ型门槛值K_(ⅠH)/K_(ⅠX)=0.29基本相同,而在K_Ⅱ/K_Ⅰ比值为0.27,0.4和0.81时,(Ⅰ+Ⅱ)复合型氢致开裂门槛值分别为0.36,0.41和0.37,表明纯Ⅰ型和纯Ⅱ型具有更高的氢脆敏感性。最后用自Ⅰ型加载向Ⅱ型过渡时,三轴张力和塑性变形程度这二个矛盾因素对氢致开裂的共同作用解释了上述实验结果。     

单晶高温合金/Al2O3型壳界面行为研究

采用直接浇注法制备金属型壳界面行为试样，其金属为单晶高温合金DD3、DD6，型壳为Al2O3。通过金相显微镜、扫描电镜及能谱分析对试样表面进行研究。结果表明，采用Al2O3型壳铸造出的DD3、DD6单晶铸件外表面光洁，Al2O3型壳可用于DD3、DD6单晶高温合金的熔模铸造工艺。     

Sn-Ag-Cu表面贴装元件的水清洗技术

采用SMT450-LD全自动SMT水清洗系统对模拟试件和贴装有片式电阻的PCB板表面残留物采用水基清洗剂清洗。结果表明，用Sn—Ag-Cu免清洗焊膏贴装在FR4基板上的片式电阻，焊后采用水基清洗剂清洗，表面残留物离子浓度为1．9μg/cm^2，达到美国军用标准MIL—STD-2000小于5．7μg／cm^2的规定。清洗过程中参数的设置，如清洗温度，清洗时间会对清洗效果产生较大影响。     

数据融合在电梯群控系统中的应用

将数据融合技术引入电梯群控系统中,建立了基于数据融合技术的模糊联结聚合神经网络模型,对影响电梯调度的各因素进行充分有效的数据处理后,得到的电梯控制参数作为电梯调度单元的输入.应用实例表明了该方法是方便且有效的.     

基于DSP320F2812的数字化CO2焊机研制

设计了数字化CO2焊机的硬件结构,并根据CO2焊接工艺的特点,编写了相应的控制软件,实现了整个焊接系统的数字化.试验结果表明,基于DSP320F2812芯片控制的焊接电源具有良好的动特性,获得了较好的控制效果,为控制策略的智能化和最优化提供了良好的平台.     

预应变对16MnR钢断裂韧性的影响SCIEI

本文实验发现预应变对16MnR钢的断裂韧性具有显著的影响,断裂过程中裂尖区域材料的组织结构发生了变化,裂纹在二次珠光体组织上扩展。16MnR钢断裂韧性的大小取决于碳原子的扩散及二次珠光体组织生成的难易程度。     

Electron beam welding of Re and BT5-1 titanium alloy

Based on the binary alloy phase diagram of Re-Ti, the weldability of Re and BT5-1 titanium alloy was analyzed. Using two methods of direct electron beam welding （EBW-D） and intergradafion electron beam welding （EBW-I）, Re and BT5-1 was welded. Experimental results show that the joint figuration of EBW-D between Re and BT5-1 is not fine, and the joint is inclined to brittleness rupture. The joint figuration of EBW-I between Re and BT5-1 is fine. No cracking and other disfigures occur in the intergradation joint. The element distribution of Re, Me, and Ti in the weld metal is progressional diversification.     

基于Visual Basic 开发机床主传动非常规变速系统的设计--重复转速的传动系统(实例之二)

本文介绍利用Visual Basic工具开发金属切削机床主传动非常规变速系统的设计总体结构，功能和方法，以重复转速的传动系统为例，重点介绍转速图的拟定过程，本系统具有界面美观，操作方便，易于理解的特点。     

盒形拉深件的CAD系统开发

阐述了运用软件工程学原理开发盒形拉深件CAD系统的整个过程，详细介绍了从盒形件拉深的工序尺寸计算到最终计算结果的输出，给出了具体的验证实例，说明了系统的可行性。